Product introduction of magnesia chrome brick
The magnesia chrome brick is made of sintered magnesium, fused magnesium and fused magnesia chrome through high-pressure molding, drying and high-temperature firing.
Features of magnesia chrome brick
The refractoriness is greater than 2000 ℃, the load softening temperature is generally above 1550 ℃, the high-temperature volume stability is good, and the resistance to quenching and heating is good.
Application of magnesia chrome brick
It is mainly used for cement rotary kilns, regenerators of glass kilns, lining of steelmaking furnaces, permanent layer of refining ladles, non-ferrous metallurgical furnaces, lime kilns, iron mixing furnaces and lining of refractory high-temperature kilns.
Parameters of magnesia chrome brick
| Model | MGe6 | MGe8 | MGe12 | MGe16 | DMGe4 | DMGe8 | DMGe12 | DMGe16 |
| MgO % | 80 | 72 | 70 | 65 | 85 | 77 | 74 | 69 |
| Cr2O3 % | 7 | 10 | 13 | 17 | 5.5 | 9.1 | 14 | 18 |
| CaO % | 1.2 | 1.2 | 1.2 | 1.2 | 1.1 | 1.4 | 1.2 | 1.2 |
| SiO2 % | 3.4 | 4 | 4 | 4.2 | 1.3 | 1.2 | 1.2 | 1.5 |
| Al2O3 % | 4.5 | 6.5 | 6 | 6 | 3.5 | 4 | 3.5 | 4.5 |
| Fe2O3 % | 4 | 4.8 | 5.5 | 6.5 | 3 | 6.4 | 5 | 5.7 |
| Apparent Porosity % | 17 | 18 | 18 | 18 | 18 | 18 | 18 | 18 |
| Bulk Density g/cm3 | 3 | 3 | 3.02 | 3.05 | 3.02 | 3.04 | 3.06 | 3.08 |
| Cold Crushing Strength Mpa | 55 | 55 | 55 | 50 | 50 | 50 | 55 | 55 |
| Refractoriness Under Load °C | 1600 | 1600 | 1600 | 1600 | 1700 | 1700 | 1700 | 1700 |
| Thermal expansion % 1000°C | / | / | / | / | 1 | 1 | 1 | 0.9 |
| Thermal expansion % 1600°C | / | / | / | / | 1.8 | 1.8 | 1.8 | 1.6 |